Amandla aphezulu kune-alumina
Iindleko eziphantsi kunezirconia
Ukumelana nokunxiba okungaqhelekanga
Ukumelana nomhlwa okuphezulu
Ukuqina kokwaphuka okuphezulu
Uzinzo oluphezulu lobushushu
Ukunxiba iilayini zerabha ezixhathisayo zisetyenziselwa ukunika ukunxiba okuphezulu kunye nokhuseleko lwempembelelo.
1) Dibanisa irabha efunxa amandla kunye ne-abrasion egqwesileyo ukumelana ne-alumina ceramic ephezulu, ilungele ukunxiba okuphezulu kunye nefuthe lezicelo.
I-2) Ubume obuqhelekileyo kunye nobukhulu ukuhlangabezana neemfuno zakho ezithile, ii-liners eziqhelekileyo kunye nezingezona eziqhelekileyo zikhona zonke.
3) Gqibezela izisombululo zokunxiba kunye ne-abrasion
I-4) Umenzi onamava atyebileyo, ibhondi elungileyo phakathi kwerubha kunye ne-ceramic, i-ceramics ihlala kwindawo de igugile ngokupheleleyo.
5) Uluhlu olubanzi lweerabha zeerabha zokunxiba iipleyiti ukuhlangabezana neemfuno zakho ezahlukeneyo.
1) Indawo yokulala
2)Yondla i-chute
3) Khupha i-chute
4)Ukugcinwa kwentsimbi
5) Hopper
6) Umgqomo
INXALENYE | IIPROPATI | IYUNITHI | ZTA Ceramic |
I-Ceramic | Al2O3 | % | 70-75 |
ZrO2 | % | 25-30 | |
Ukuxinana | g/cm3 | 4.20 | |
Vickers ubulukhuni | Kg/mm2 | 1300 | |
Ukuqina kokwaphuka | Mpa.M1/2 | 3-4 | |
Irabha | Amandla e-Flexural | Mpa | 680 |
Ukuqamba | - | Irabha yendalo+SBR | |
Ukuqina konxweme | HA | 60±5 | |
Isantya sobude bokuqina | % | >400 | |
Tensile strength | Mpa | 25 | |
Amandla eenyembezi(%) | % | 30 | |
Amandla okudibanisa phakathi kwerabha kunye ne-ceramic | Mpa | 4 | |
Intsimbi | Izinto eziphathekayo | - | Q235A |
Amandla okuqina Uxinzelelo | g/cm3 | 7.85 | |
Ukutyeba | mm | 5-6 | |
Ukuncamathelisa | Imbonakalo | - | Ulwelo olumdaka olumdaka |
Umxholo oqinileyo | - | 20±3% | |
Viscosity | Mpa | ≥2.5 | |
Amandla e-Peel | 48h N/2.5cm | ≥120 | |
Amandla acinezelayo | Mpa | ≥850 | |
Ubushushu bokusebenza | ºC | -20 - 100 |